OK 61.85是一款适用于E347牌号的碱性药皮铌稳定化焊条,其非常适用于焊接铌稳定化或钛稳定化钢种。OK 61.85在立焊和仰焊位置使用时具有出色的焊接性能,因而非常适用于管道焊接。
Typical Tensile Properties
As welded |
Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
Stress Relieved Temperature |
Stress Relieved Testing Time |
40 % |
620 MPa |
500 MPa |
ISO |
- |
- |
Stress relieved |
Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
Stress Relieved Temperature |
Stress Relieved Testing Time |
40 % |
640 MPa |
500 MPa |
ISO |
600 °C |
16 hr |
As welded |
Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
Stress Relieved Temperature |
Stress Relieved Testing Time |
- |
- |
- |
AWS |
- |
- |
夏比V型缺口冲击性能
As welded |
Impact Value |
Testing Temperature |
保护气体 |
Stress Relieved Testing Temp |
Stress Relieved Testing Time |
100 J |
20 °C |
ISO |
- |
- |
70 J |
-60 °C |
ISO |
- |
- |
- |
-120 °C |
ISO |
- |
- |
Stress relieved |
Impact Value |
Testing Temperature |
保护气体 |
Stress Relieved Testing Temp |
Stress Relieved Testing Time |
80 J |
20 °C |
ISO |
600 °C |
16 hr |
40 J |
-60 °C |
ISO |
600 °C |
16 hr |
焊缝金属分析
Mn |
Mn |
C |
Nb |
Si |
Ferrite FN |
Ni |
N |
Cr |
1.7 % |
- |
- |
- |
- |
- |
- |
- |
C |
Mn |
C |
Nb |
Si |
Ferrite FN |
Ni |
N |
Cr |
- |
0.04 % |
- |
- |
- |
- |
- |
- |
Nb |
Mn |
C |
Nb |
Si |
Ferrite FN |
Ni |
N |
Cr |
- |
- |
0.61 % |
- |
- |
- |
- |
- |
Si |
Mn |
C |
Nb |
Si |
Ferrite FN |
Ni |
N |
Cr |
- |
- |
- |
0.4 % |
- |
- |
- |
- |
Ferrite FN |
Mn |
C |
Nb |
Si |
Ferrite FN |
Ni |
N |
Cr |
- |
- |
- |
- |
6 % |
- |
- |
- |
Ni |
Mn |
C |
Nb |
Si |
Ferrite FN |
Ni |
N |
Cr |
- |
- |
- |
- |
- |
10.2 % |
- |
- |
Cr |
Mn |
C |
Nb |
Si |
Ferrite FN |
Ni |
N |
Cr |
- |
- |
- |
- |
- |
- |
- |
19.5 % |
熔敷数据
Fusion time per electrode at 90% I max |
kg weld metal/kg electrodes |
Number of electrodes/kg weld metal |
安培 |
熔敷率 |
电压 V |
直径 |
42 sec |
0.60 kg |
98 |
55-80 A |
0.9 kg/h |
25 V |
2.5 x 300 mm |
64 sec |
0.62 kg |
49 |
75-110 A |
1.2 kg/h |
23 V |
3.2 x 350 mm |
70 sec |
0.61 kg |
33 |
80-150 A |
1.6 kg/h |
24 V |
4.0 x 350 mm |
76 sec |
0.61 kg |
21 |
150-200 A |
2.3 kg/h |
23 V |
5.0 x 350 mm |
|